C17200 Beryllium Copper Sheet

Beryllium copper alloys are used in a variety of applications including automotive industrial and oil gas drilling.

C17200 beryllium copper sheet.

Beryllium copper c172 c17200 alloy 25 astm b196 ams 4533 din 2 1247 bs 2870 cb101 bs 2871 cb101 bs 2874 cb101 en cw101c farmer s copper ltd. Beryllium copper combines high strength with non magnetic and non sparking. Commonly stocked beryllium copper. Balance physical properties elastic modulus melting point solidus electrical conductivity resistivity density thermal expansion coefficient thermal conductivity 25 c 19 000 ksi 131 gpa 1600 f 870 c 22 28 iacs 6 2 7 8 μωcm.

It is generally recommended as electrode material for special flash flash butt and projection welding applications where pressures are extremely high and wear is severe but where heating is. Copper alloy c17200 is the most commonly specified copper beryllium alloy. The application of powertrain materials in automobiles and commercial vehicles. C17200 beryllium copper has extremely high hardness and ultimate tensile strength although the electrical conductivity is lower than the class 3 copper.

Beryllium copper c172 is also known as alloy 25 sheet and c17200 sheet. Full hard and mill hardened tempers are stocked on a limited basis. Busby metals is your go to beryllium supplier. C17200 copper cda 172 astm b196 ams 4533 sae j461 rwma class iv.

The ultimate tensile strength can exceed 200 ksi while the hardness approaches rockwell c45. Inventories c17200 beryllium copper. 17410 17460 and 17510 are also obtainable. C17200 copper beryllium alloy.

The quality inspection of beryllium copper products. Mechanical properties form temper temper code tensile strength ksi ys 0 2 offset elongation rockwell b scale rockwell c scale rockwell 30t scale. In its age hardened condition it attains the highest strength and hardness of any commercial copper base alloy. C17200 is also known as alloy 25 and is the most commonly utilized beryllium copper alloy and is notable for exhibiting the highest strength and hardness compared to commercial copper alloys.